| 基本信息 | |
|---|---|
| 机构评级 |
|
| 形式 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 0.924 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 51 | μm | |
| 膜耐刺穿性 (51 μm) | 5.46 | J/cm3 | 内部方法 |
| 膜强度 | ASTM D882 | ||
| MD : 51 μm | 94.5 | J/cm3 | ASTM D882 |
| TD : 51 μm | 94.9 | J/cm3 | ASTM D882 |
| 割线模量 | ASTM D882 | ||
| 1% 正割, MD : 51 μm | 250 | MPa | ASTM D882 |
| 1% 正割, TD : 51 μm | 272 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 51 μm | 15.4 | MPa | ASTM D882 |
| TD : 屈服, 51 μm | 14.2 | MPa | ASTM D882 |
| MD : 断裂, 51 μm | 30.2 | MPa | ASTM D882 |
| TD : 断裂, 51 μm | 25.4 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 51 μm | 440 | % | ASTM D882 |
| TD : 断裂, 51 μm | 600 | % | ASTM D882 |
| 落锤冲击 (51 μm) | 120 | g | ASTM D1709A |
| 埃尔曼多夫抗撕强度 1 | ASTM D1922 | ||
| MD : 51 μm | 280 | g | ASTM D1922 |
| TD : 51 μm | 570 | g | ASTM D1922 |
高压低密度聚乙烯(high pressure-low density polyethylene，HP-LDPE，简写为LDPE)实现工业化已有70多年的历史，尽管随着烯烃聚合催化剂的发现与发展，聚乙烯的品种和产量有了巨大的进展，但高压聚乙烯仍占有重要的地位。乙烯在高温高压下以自由基机理聚合成高分子量聚乙烯，具有以下特点：
(1)乙烯聚合反应过程是一个强烈的放热过程。乙烯的聚合热约为93.5kJ/mol(或3.3kJ/g)，在235MPa、150~300℃下乙烯的比热容为2.51~2.85J/(g·℃)，反应热如果不能及时移去，每1%乙烯发生聚合将使温度升高12~13℃。如果温度过高，还会导致乙烯分解。
(2)在高压下，乙烯 已被压缩到密度为0.5g/mL的气密相状态，近似于不能再压缩的液体，此时乙烯分子间的距离显著缩短，从而增加了游离基与乙烯分子的碰撞概率，所以容易发生聚合反应。
(3)高温下增长链的自由基活性大，容易发生链转移反应，所得到的聚合物为带有较多支链的线型结构 。通常每1000个碳链原子中含有20~30个支链 ，结晶度 为45%~65%，密度在0.910~0.925g/mL，质轻、具柔性，耐低温性、耐冲击性较好。